TC11 BT9 titanium alloy rod bar Ti-6.5Al-3.5Mo-1.5Cr-0.3Si price per kg
| Product name | Titanium rod / Titanium bar |
| Grade | BT9 (Ti-6.5Al-3.5Mo-1.5Cr-0.3Si) |
| Standard | ASTM B348 , AMS4928 |
| Dimention | Diameter:3.0-500mm
Length:500-6000mm, or as customer's request Tolerance:H7-H11, h7-h11 |
| Surface | Polished |
| Technique | Rolled, forged |
| Application | Metallurgy, electronics, medical, chemical, petroleum etc. |
| Main chemical composition | Impurities <= |
| Al | Mo | Zr | Si | Ti | Fe | C | N | H | O | Others |
| Each | Total |
| 5.8～7.0 | 2.8～3.8 | 0.8～2.0 | 0.20～0.35 | Remiander | 0.25 | 0.08 | 0.05 | 0.012 | 0.15 | 0.10 | 0.4 |
| Tensile requirements |
| grade | Tensile strength(min) | Yeild strength(min) | Elongation(%) |
| ksi | MPa | ksi | MPa |
| 1 | 149 | 1030 | 131 | 900 | 10 |
Ti-6.5Al-3.5Mo-1.5Zr-0.3Si is an α-β type titanium alloy heat-resistant titanium alloy with aluminum equivalent
3.5 and molybdenum equivalent 7.3. The alloy also has good hot workability (including conventional process
performance and superplasticity), and can be welded and machined in various ways. The beta heat treatment
and isothermal forging of this alloy have achieved rapid development.
The alloy is mainly used for the manufacture of compressor disks, blades, drums and other parts of aircraft engines,
and can also be used to manufacture aircraft structural parts. Through the thermal deformation and heat treatment
in the α-β region, the maximum long-term working temperature of the alloy is 500 ° C. The semi-finished products
produced include bars, forgings and die forgings.
Ti-6.5Al-3.5Mo-1.5Cr-0.3Si titanium alloy is a widely used high-temperature titanium alloy with a maximum operating temperature of 500 ° C.
It is mainly used in aircraft engine compressor components such as blades, discs, drums and shafts. It can also be
made into special-shaped castings. The working conditions of the parts are that they can be used for 500 hours below
500 ° C and 100 hours below 550 ° C and 1000 hours below 450 ° C in the annealed state, and can be used for 100
hours below 500 ° C in the strengthening treatment Parts and parts that work at a time below 700 ℃.
Products pictures:
Packing and Shipping:
Our company strictly follows the standard export packaging and to package goods. Inside is pearl cotton
and foam film to reduce the impact and friction of the cargo. Goods under 10kg are generally packed in cartons;
goods over 10kg are generally packed in wooden boxes. The inside and outside of the packaging box are kept clean.
The outer packaging is wrapped with tape or steel strips--- very strong and firm to ensure that the goods are intact
when the customer receives them.
The courier companies we long-term cooperated mainly include FedEx, DHL, TNT, UPS etc.
Air and sea shipping ,we always choose safe and speed international routes.
For transportation, we always choose different express and routes according to customers in different countries
to save purchasing costs for customers.
Baoji Lihua Non-ferrous Metals Co., Ltd, founded in 2006, lies in Tai Cheng road Baoji city---It is famous for
manufacturing titanium, called “China Titanium Valley”.We are specialized in manufacturing, researching and
marketing for titanium. With over 14 years export Experience, our products was sold to Asia, Europe, North America
in large quantity.In addition to provide preferential price for customers, we pay much attention to quality, and
have a good after-sales service.All products we produced are based on the standard: German standard ,Aerospace
standard, European standard, etc,including ANSI/ASTM, JIS , DIN etc.
Lihua is certified by ISO9001:2008 and IQNET. Our company have long-term cooperated with international inspection
agency, such as SGS,BV, LR'S ,TUV etc.Welcome customers to do the third party test to our products.
Welcome to contact!
Product Tags:
|
|
Annealed TC11 BT9 Titanium Alloy Bar Ti-6.5Al-3.5Mo-1.5Cr-0.3Si 500-6000mm Length Images
|